ASTM A790 S31803 Duplex Seamless And Welded Pipe Corrosion Resistant
UNS S31803, F51, 1.4462 duplex stainless steel is designed to combine improved resistance to stress corrosion cracking, pitting, crevice corrosion and high strength when compared with other stainless alloys.
These attributes mean that Duplex UNS S31803, F51, 1.4462 can be used successfully as an alternative to standard stainless steel specifications in applications where higher strength and resistance to stress corrosion cracking is required.
Chemical Composition of S31803
| Property | Value |
| Carbon | 0.03% |
| Chromium | 21-23% |
| Manganese | 2% |
| Molybdenum | 2.5-3.5% |
| Nickel | 4.5-6.5% |
| Nitrogen | 0.08-0.02% |
| Phosphorus | 0.03% |
| Silicon | 1% |
| Sulfur | 0.02% |
Mechanical Behaviour
| Property | Value |
| Tensile Strength, min, ksi, [MPa] | 90 [ 620] |
| Yield Strength, min, ksi [MPa] | 65 [450] |
| Elongation in 2 in. or 50mm, min, % | 25 |
| Hardness, max | HBW | HRC |
| 290 | 30 |
Tolerances Of ASTM A790 UNS S31803 Pipe
| NPS Designator | Permissible Variations in Outside Diameter |
| Over In. | Under In. |
| 1/8 to 1-1/2, incl | 1/64 (0.015) | 1/32 (0.031) |
| Over 1-1/2 to 4, incl | 1/32 (0.031) | 1/32 (0.031) |
| Over 4 to 8, incl | 1/16 (0.062) | 1/32 (0.031) |
| Over 8 to 18, incl | 3/23 (0.093) | 1/32 (0.031) |
Pressure Rating
| Pipes O.D. (in.) | Duplex Steel 2205 Pipe Wall Thickness of Pipe (inches) |
| .035 | .109 | .028 | .065 | .049 | .095 | .083 | .120 |
| 1/4 | 4800 | | 3700 | 9500 | 7000 | | | |
| 1/8 | 10100 | | 7900 | | | | | |
| 3/8 | 3100 | | | 6100 | 4400 | | | |
| 5/16 | 3700 | | | 7300 | 5400 | | | |
| 3/4 | | | | 3000 | 2200 | 4600 | 4000 | |
| 1/2 | 2300 | | | 4400 | 3200 | | | |
| 1 | | 3900 | | 2200 | | 3400 | 2900 | 4300 |
Duplex Stainless Steel Features
Duplex stainless steels have Austenitic and Ferritic stainless steel microstructure, and possess properties in two groups stainless steel, however, there are different.
Versus Austenitic
- Higher yield strength
- Greater corrosion resistance
- Stress corrosion cracking resistance
- Not common, used temperate under 250 C.
- Fabricability not good as Austenitic
- Strictly control heat treatment and welding process
- Price stability
Versus Ferritic
- Good toughness than Ferric, not hard
- Greater corrosion
- Fabricability is better
- Better weldability
- Wide usage than Ferritic
- Higher price
APPLICATIONS:
· Chemical processing, transportation and storage
· Oil and gas exploration and offshore drilling rigs
· Oil and gas refining
· The marine environment
· Pollution control equipment
· Pulp and paper manufacturing
· Chemical process plant